Laminating Resin

Filter

Application

1. Good wetting and impregnating. Pot life and cure time can be varied by using a mixture of H3 & H8 keeping the same mixing ratio. This can be used for thicker laminates. (1)
2. Very low viscosity modified laminating resin. (1)
3. Very low viscosity producing good wetting of fibres and fillers. (1)

Pot Life (200g, 25°C) minutes

1. 160-220 (2)
2. 18-24 (1)
3. 20-25 (1)
4. 30-50 (1)
5. 30-60 (1)
6. 300-360 (1)
7. 40-70 (1)
8. 45-60 (1)
9. 50-70 (2)
10. 60-80 (1)
11. See TDS (8)

Cure Time (25°C) Hours

1. 12 (2)
2. 16-24 (1)
3. 18-24 (1)
4. 24 (6)
5. 24-48 (1)
6. 48 (1)
7. 8-14 (1)
8. See TDS (7)

Viscosity (25°C) mPa.s

1. 1100-1500 (2)
2. 150-250 (1)
3. 180-300 (1)
4. 2000-3000 (1)
5. 250-450 (1)
6. 300-600 (2)
7. 450-650 (1)
8. 500-1200 (1)
9. 500-800 (1)
10. 900-1300 (1)
11. See TDS (8)

HDT °C

1. 103-109 (1)
2. 108-112 (1)
3. 133-139 (1)
4. 170 (1)
5. 56-60 (1)
6. 57-61 (1)
7. 60-65 (1)
8. 63-67 (1)
9. 76-80 (1)
10. 79-83 (1)
11. 82-86 (1)
12. 88-92 (1)
13. n/a (1)
14. See TDS (7)

Shore Hardness

1. 78-82D (3)
2. 80-90A (1)
3. 82-87D (2)
4. 83-87 (1)
5. 83-87D (4)
6. 85-88D (1)
7. 85-90D (4)
8. 87-92 (1)
9. See TDS (3)